UmaPET TF
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Ester Industries Ltd. |
| Trademark: | UmaPET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gSGyIE_UmaPET-TF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
KEY FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | ASTM D1204 | ||
| Flow : 150°C, 30 min, 0.0100 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0120 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0150 mm | 2.5 | % | |
| Flow : 150°C, 24 hr, 0.0190 mm | 2.0 | % | |
| Flow : 150°C, 30 min, 0.0230 mm | 2.0 | % | |
| Across Flow : 150°C, 30 min, 0.0100 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0120 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0150 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0190 mm | 0.40 | % | |
| Across Flow : 150°C, 30 min, 0.0230 mm | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 1 | 0.42 | ||
| vs. Itself - Dynamic 2 | 0.45 | ||
| vs. Itself - Dynamic 3 | 0.45 | ||
| vs. Itself - Dynamic 4 | 0.45 | ||
| vs. Itself - Dynamic 5 | 0.42 | ||
| vs. Itself - Static 6 | 0.48 | ||
| vs. Itself - Static 7 | 0.50 | ||
| vs. Itself - Static 8 | 0.50 | ||
| vs. Itself - Static 9 | 0.50 | ||
| vs. Itself - Static 10 | 0.48 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 10 12 15 19 23 | µm | |
| Film Thickness - Recommended / Available | 10, 12, 15, 19, 23 µm | ||
| Tensile Strength | ASTM D882 | ||
| MD : Break, 10 µm | 206 | MPa | |
| MD : Break, 12 µm | 206 | MPa | |
| MD : Break, 15 µm | 186 | MPa | |
| MD : Break, 19 µm | 186 | MPa | |
| MD : Break, 23 µm | 186 | MPa | |
| TD : Break, 10 µm | 216 | MPa | |
| TD : Break, 12 µm | 216 | MPa | |
| TD : Break, 15 µm | 206 | MPa | |
| TD : Break, 19 µm | 206 | MPa | |
| TD : Break, 23 µm | 206 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 10 µm | 100 | % | |
| MD : Break, 12 µm | 100 | % | |
| MD : Break, 15 µm | 100 | % | |
| MD : Break, 19 µm | 100 | % | |
| MD : Break, 23 µm | 100 | % | |
| TD : Break, 10 µm | 90 | % | |
| TD : Break, 12 µm | 90 | % | |
| TD : Break, 15 µm | 90 | % | |
| TD : Break, 19 µm | 90 | % | |
| TD : Break, 23 µm | 90 | % | |
| Yield | Internal Method | ||
| 10.0 µm | 71.4 | m²/kg | |
| 12.0 µm | 59.5 | m²/kg | |
| 15.0 µm | 47.6 | m²/kg | |
| 19.0 µm | 37.6 | m²/kg | |
| 23.0 µm | 31.0 | m²/kg |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Wetting Tension - Plain side | ASTM D2578 | ||
| 10.0 µm | 44 | dyne/cm | |
| 12.0 µm | 44 | dyne/cm | |
| 15.0 µm | 44 | dyne/cm | |
| 19.0 µm | 44 | dyne/cm | |
| 23.0 µm | 44 | dyne/cm |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | ASTM D1003 | ||
| 10.0 µm | 3.5 | % | |
| 12.0 µm | 3.5 | % | |
| 15.0 µm | 3.5 | % | |
| 19.0 µm | 4.0 | % | |
| 23.0 µm | 4.5 | % |
| Note Message | |
|---|---|
| 1 . | 23 µm |
| 2 . | 15 µm |
| 3 . | 12 µm |
| 4 . | 10 µm |
| 5 . | 19 µm |
| 6 . | 19 µm |
| 7 . | 15 µm |
| 8 . | 12 µm |
| 9 . | 10 µm |
| 10 . | 23 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3703C | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Maxelast® P3960 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TechnoElast 9080 | TechnoCompound GmbH | SEBS | TechnoElast |
| Karina IVORY PVC COMPOUND 90850-35/1-AY-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJORIS EFR210R - 8229 | AD majoris | PP, Unspecified | MAJORIS |