Sumikon® PM-6630 (Type: J Black)
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gS02Zc_SumikonPM6630TypeJBlack.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON PM-6630 Type J Black is a Short Glass fiber & Mineral molding compound based on Phenolic Novolac polymer. It is supplied in the form of Granular/Molding Powder for Molding. This grade is official registered UL with V-0 (t=3.0). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.79 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.20 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 15600 | MPa | JIS K6911 |
| Flexural Strength | 207 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.3 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 216 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 10 | kV/mm | JIS K6911 |
| Insulation Resistance 2 | 5.0E+11 | ohms | JIS K6911 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| 2 . | As molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPC 7712 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| FINGERPRINT™ MDPE 7520 NT | The Dow Chemical Company | MDPE | FINGERPRINT™ |
| Kotex KG-30F15 | Kotec Corporation | PC | Kotex |
| LONGLITE® PBT 6015-104X | CCP Group | PC+PBT | LONGLITE® PBT |
| Hostacom EKC 265N 2 C12594 | LyondellBasell Industries | PP Copolymer | Hostacom |