Lupoy® 1320C-07
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gRrvy4_Lupoy-1320C-07.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUPOY PC 1320C-07 resin provides stability against ultraviolet radiations to solid or multi-wall sheets via the co-extrusion of a 50 µm thick layer |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2000 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 60.0 | MPa | |
| Break | 68.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 110 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 4.00 mm) | 130 | °C | ASTM D648 |
| Vicat Softening Temperature | 138 | °C | ASTM D1525 4 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance | 73.0 | % | ASTM D1003 |
| Haze | 0.70 to 1.5 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9462-80 Black | Sylvin Technologies Incorporated | PVC Alloy | Sylvin |
| Moplen RP348N | LyondellBasell Industries | PP Random Copolymer | Moplen |
| DAULEN PPC GF 30 | Daunia Trading srl | PP Impact Copolymer | DAULEN |
| Generic ABS - Carbon Fiber | Generic | ABS | Generic |
| POTICON VCF442 | Otsuka Chemical Co., Ltd. | LCP | POTICON |