PRL TP-FR2
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gRKg2g_PRL-TP-FR2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL TP-FR2 is a Polybutylene Terephthalate (PBT) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 10 to 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 to 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 57.9 | MPa | |
| Break, 3.18 mm | 57.9 | MPa | |
| Flexural Modulus (3.18 mm) | 2590 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 149 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 68.3 | °C | |
| RTI Elec | UL 746 | ||
| 0.800 mm | 130 | °C | |
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 0.800 mm | 120 | °C | |
| 1.50 mm | 120 | °C | |
| 3.00 mm | 120 | °C | |
| RTI Str | UL 746 | ||
| 0.800 mm | 130 | °C | |
| 1.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (0.800 mm) | 39 | kV/mm | ASTM D149 |
| Arc Resistance (0.800 mm) | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) (0.800 mm) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 0.800 mm | PLC 0 | ||
| 1.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| High Voltage Arc Tracking Rate (HVTR) (0.800 mm) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 0.800 mm | PLC 4 | ||
| 1.50 mm | PLC 3 | ||
| 3.00 mm | PLC 2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm, ALL | V-0 | ||
| 1.50 mm, ALL | V-0 | ||
| 3.00 mm, ALL | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 232 to 249 | °C | |
| Middle Temperature | 238 to 254 | °C | |
| Front Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 43.3 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PGR2446 | Spartech Polycom | PP Homopolymer | Spartech |
| Stanyl® 46HF5041LW | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| NYCOA Polyamide 870 | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| CP PRYME® Acetal AC100-9 | Chase Plastics Services Inc. | Acetal (POM) Copolymer | CP PRYME® Acetal |
| Karina BLACK PVC COMPOUND 825-48/ 1-DY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |