Fortron® 1140E7
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gRG9o4_Fortron-1140E7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron 1140E7 is an inherently flame-retardant grade exhibiting extremely low flash and fast cycle times. It has excellent electrical properties, high hardness and stiffness. This grade exhibits good high-temperature load-bearing capabilities. It is especially used for thinner walled and longer flow length parts requiring low flash behavior. Good weldability due to a modest filler level. Commonly used in electrical connectors and other thin wall/long flow length parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.60 | g/cm³ | ASTM D792 |
| -- | 1.65 | g/cm³ | ISO 1183 |
| Specific Volume | 0.611 | cm³/g | ASTM D792 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specimen Thickness - Shrinkage | 3.18 | mm | Internal method |
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | |||
| Flow | 0.20 - 0.30 | % | ASTM D955 |
| Transverse flow | 0.50 - 0.70 | % | ASTM D955 |
| Vertical flow direction | 0.40 - 0.60 | % | ISO 294-4 |
| Flow direction | 0.20 - 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class m | 103 | ASTM D785 | |
| M scale | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15700 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 152 | MPa | ASTM D638 |
| Fracture | 150 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.4 | % | ASTM D638 |
| Fracture | 1.2 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 15000 | MPa | ISO 178 |
| Flexural Stress 1 | 230 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 28 | kJ/m² | ISO 179/1eU |
| 23°C | 28 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, annealed | 280 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 270 | °C | ASTM D648, ISO 75-2/A |
| 8.0 MPa, not annealed | 215 | °C | ISO 75-2/C |
| Glass Transition Temperature 2 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature | |||
| -- 3 | 280 | °C | ISO 11357-3 |
| -- | 282 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+17 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | 25 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 kHz | 3.70 | ASTM D150 | |
| 1 MHz | 3.70 | ASTM D150 | |
| 1 MHz | 4.70 | IEC 60250 | |
| Dissipation Factor | |||
| 1 kHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 1.0E-3 | ASTM D150 | |
| 1 MHz | 0.020 | IEC 60250 | |
| Arc Resistance | 134 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.850 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 | |
| Oxygen Index | 47 | % | ASTM D2863, ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | Break |
| 2 . | 10°C/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP562S | PolyMirae | PP Homopolymer | Moplen |
| THERMOLAST® K TF7BNA (Series: FC/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Titacon® TF410 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Homopolymer | Titacon® |
| Nypol® PA B3 HL CNZ0311 NT362 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Sumikon® AM-3500 | SBHPP | DAP | Sumikon® |