Infino HX-4300G
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gQxUOA_Infino-HX-4300G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino HX-4300G is a Polyphthalamide (PPA) product filled with glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (330°C/2.16 kg) | 25 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.45 to 0.55 | % | |
| Across Flow : 3.20 mm | 0.57 to 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8300 | MPa | ASTM D638 |
| -- | 9600 | MPa | ISO 527-2/5 |
| Tensile Strength | |||
| Yield 2 | 170 | MPa | ASTM D638 |
| Yield | 160 | MPa | ISO 527-2/5 |
| Break 3 | 170 | MPa | ASTM D638 |
| Break | 170 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 4 | 3.0 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- 5 | 9800 | MPa | ASTM D790 |
| -- 6 | 10600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 220 | MPa | ASTM D790 |
| -- 8 | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 64 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 69 | J/m | ASTM D256 |
| 23°C 10 | 8.3 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 290 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 290 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index | 1 PLC | IEC 60112 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.400 to 3.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 280 to 290 | °C | |
| Middle Temperature | 300 to 310 | °C | |
| Front Temperature | 320 to 330 | °C | |
| Nozzle Temperature | 330 | °C | |
| Mold Temperature | 100 to 140 | °C | |
| Injection Pressure | 108 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 GRF 2318 H | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| XYRON™ TT520 | Asahi Kasei Chemicals Corporation | PPE+PP | XYRON™ |
| DENYL 66 N | Vamp Tech | Nylon 66 | DENYL |
| Ebalta MG 709-120 / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Plaslube® PC / ASA FR1508 UV | Techmer Engineered Solutions | ASA+PC | Plaslube® |