Bapolene® LL100F
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Bamberger Polymers, Inc. |
| Trademark: | Bapolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gQCSD6_Bapolene-LL100F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bapolene LL100F is a general purpose LLDPE for blown film extrusion applications. This resin exhibits excellent tensile and toughness properties. Contains medium levels of slip/antiblock additives. This product meets FDA standards for food contact applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| MD | 214 | MPa | ASTM D882 |
| TD | 248 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 15.9 | MPa | ASTM D882 |
| TD : Yield | 16.7 | MPa | ASTM D882 |
| MD : Fracture | 38.6 | MPa | ASTM D882 |
| TD : Fracture | 29.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 560 | % | ASTM D882 |
| TD : Fracture | 750 | % | ASTM D882 |
| Dart Drop Impact (38 µm) | 130 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 250 | g | ASTM D1922 |
| TD : 38 µm | 620 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 14 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Thickness, 2:1 blow-up ratio: 37.5µmGloss, ASTM D2457: 45%Secant Modulus, ASTM D882, MD, 0.1 mm/mm/min initial strain rate: 214MPaSecant Modulus, ASTM D882, TD, 0.1 mm/mm/min initial strain rate: 248 MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 - 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK CC200 (KD2190) | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| Sinpolene GPP1615/2 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| SUMIKASUPER® LCP E4006L | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| Kumho SSBR SOL-5250H | Korea Kumho Petrochemical Co., Ltd. | SBR, Solution | Kumho SSBR |
| Lucent PP TPP-217Q | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |