NORYL™ NH7010HF resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gPiEbC_NORYL-NH7010HF-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Noryl* NH7010HF resin is a modified PPE-PS blend that exhibits an excellent balance of non-halogenated flame retardance, high heat resistance, good flow, and low specifc gravity for light weight parts. The resin will be available in custom colors and is suitable for injection molding. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.80 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.25 | % | |
| Equilibrium, 23°C, 50% RH | 0.050 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2180 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 59.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 12 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2460 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 69 | J/m | |
| 23°C | 230 | J/m | |
| Instrumented Dart Impact (23°C, Total Energy) | 53.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 6 | 139 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 159 | °C | ASTM D1525 7 |
| -- | 162 | °C | ISO 306/B120 |
| Ball Pressure Test 8(145°C) | Pass | IEC 60695-10-2 | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.0E-5 | cm/cm/°C | |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI Str | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance 9 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, Testing by SABIC | V-0 | ||
| 2.00 mm, Testing by SABIC | 5VA | ||
| Glow Wire Flammability Index (1.50 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 825 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 266 to 316 | °C | |
| Middle Temperature | 277 to 321 | °C | |
| Front Temperature | 288 to 327 | °C | |
| Nozzle Temperature | 299 to 327 | °C | |
| Processing (Melt) Temp | 299 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 mm |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| 8 . | Approximate maximum |
| 9 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPC1CF2-Black | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Elastron® G G500.A50.N.PA | Elastron USA, Inc. | SEBS | Elastron® G |
| HI-ZEX™ 540E | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| Karina BLACK PVC COMPOUND TR-551D48/1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| JSR EPR EBM2021P | JSR Corporation | EPDM | JSR EPR |