IROGRAN® PS440-202
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gPYdfh_IROGRAN-PS440-202.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN PS440-202 is a high performance polyester based thermoplastic polyurethane intended for extrusion and injection molding applications. IROGRAN PS440-202 is part of the HUNTSMAN film and sheet / technical extrusion product range and offers a specially designed, flexible material with a broad processing window particularly suitable for film and sheet, and textile laminations, polyblends, and industrial articles. PERFORMANCE FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.21 | g/cm³ | ASTM D792, DIN 53478 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Injection Molded) | 88 | ASTM D2240, DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | |||
| -- | 30 | mm³ | DIN 53516 |
| -- | 29 | mm³ |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| TMA 3 | Internal Method | ||
| High : 635.0 µm | 168 | °C | |
| Low : 635.0 µm | 141 | °C |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 4 | DIN 53504 | ||
| 100% Strain, 0.635 mm | 5.60 | MPa | |
| 300% Strain, 0.635 mm | 10.0 | MPa | |
| Tensile Stress 5(Break, 0.635 mm) | 48.0 | MPa | DIN 53504 |
| Tensile Elongation 6(Break, 0.635 mm) | 650 | % | DIN 53504 |
| Tear Strength 7(0.635 mm) | 62 | kN/m | DIN 53515 |
| Compression Set 8 | |||
| 23°C, 70 hr | 30 | % | ASTM D395, DIN 53517 |
| 70°C, 24 hr | 80 | % | ASTM D395 |
| 70°C, 24 hr | 60 | % | DIN 53517 |
| Bayshore Resilience | 30 | % | ASTM D2632 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 45.0 to 55.0 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 180 | °C | |
| Cylinder Zone 1 Temp. | 190 | °C | |
| Cylinder Zone 2 Temp. | 190 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 190 | °C | |
| Adapter Temperature | 190 | °C | |
| Die Temperature | 190 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Extruded Film |
| 4 . | Extruded Film |
| 5 . | Extruded Film |
| 6 . | Extruded Film |
| 7 . | Extruded Film |
| 8 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® D black EL | Röchling Engineering Plastics SE & Co. KG | HMWPE | POLYSTONE® |
| Small Boss SPVC003 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Flexible | Small Boss |
| TAISOX 9007 | Formosa Plastics Corporation | HDPE | TAISOX |
| BCC Resins MB5000 | BCC Products Inc. | PUR, Unspecified | BCC Resins |
| LEXAN™ HFD4412 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |