Geon™ HTX M6307
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gPMyIE_Geon-HTX-M6307.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon™ HTX M6307 is a Polyvinyl Chloride Alloy (PVC Alloy) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Geon™ HTX M6307 include outdoor applications, construction applications, electrical/electronic applications and wire & cable. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Spiral Flow | 76.2 | cm | |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Outdoor Suitability (Gray) | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1720 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 29.6 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 94 | % | ASTM D638 |
| Flexural Modulus | 1790 | MPa | ASTM D790 |
| Flexural Strength | 50.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| -40°C, 3.18 mm, Injection Molded | 160 | J/m | |
| -18°C, 3.18 mm, Injection Molded | 370 | J/m | |
| 0°C, 3.18 mm, Injection Molded | 590 | J/m | |
| 23°C, 3.18 mm, Injection Molded | 750 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 73.9 | °C | |
| 0.45 MPa, Annealed, 6.35 mm | 81.1 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 68.9 | °C | |
| 1.8 MPa, Annealed, 6.35 mm | 73.9 | °C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (2.01 mm, ALL) | V-0 5VA | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| QUV Weatherometer 4 | 0.58 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 68.3 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 202 to 207 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | 351 Lamp, All Colors, detla E (CIE), 24 hrs light, 300 hrs, No Moisutre |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECOLITE KM-747(J) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| Moplen HP450J | PolyMirae | PP Homopolymer | Moplen |
| TITANPRO® SM388 | Lotte Chemical Titan (M) Sdn. Bhd. | PP Random Copolymer | TITANPRO® |
| Laticonther 47/1 CP/80 | LATI S.p.A. | PP Copolymer | Laticonther |
| Hy-Vin® XN78036 | INEOS Compounds | PVC, Flexible | Hy-Vin® |