Ultron® 150C4

Category:	PEI , Polyether Imide
Manufacturer:	Asia International Enterprise (Hong Kong) Limited
Trademark:	Ultron®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	gPE5rX_Ultron-150C4.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polyetherimide (Abbr. PEI) is a high performance amorphous engineering polymer offers excellent thermal resistance, broad chemical resistance, inherent flame retardant properties, very good dimensional stability, high strength and stiffness, excellent abrasion resistance, good wave transmittance, outstanding electrical properties. PEI well balances mechanical properties and processability, offering flexibility and efficiency in applications of electronic and electrical industries, mechanical and chemical industries, automotives, aerospace. PEI also used to replace metal parts for traditional and household products.

General Information
Filler / Reinforcement	Carbon Fiber, 20% Filler by Weight
Features	Amorphous Flame Retardant Good Abrasion Resistance Good Chemical Resistance Good Dimensional Stability Good Electrical Properties Good Flexibility Good Processability High Heat Resistance High Stiffness High Strength
Uses	Aerospace Applications Automotive Applications Electrical/Electronic Applications Household Goods Metal Replacement
Agency Ratings	EU Food Contact, Unspecified Rating FDA Food Contact, Unspecified Rating
Forms	Pellets

Physical	Nominal Value	Unit	Test Method
Density	1.31	g/cm³	ISO 1183
Molding Shrinkage			ISO 294-4
Across Flow	0.30	%
Flow	0.10	%
Water Absorption (Saturation, 23°C)	0.20	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	118		ISO 2039-2

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	180	MPa	ISO 527-2/1270
Tensile Strain (Break)	2.5	%	ISO 527-2/50
Flexural Modulus ¹	12000	MPa	ISO 178
Flexural Stress ²	250	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact Strength	12	kJ/m²	ISO 180
Unnotched Izod Impact Strength	45	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	207	°C	ISO 75-2/A
Vicat Softening Temperature	218	°C	ISO 306/B50
CLTE - Flow (-20 to 150°C)	3.2E-4	cm/cm/°C	ISO 11359-2
Thermal Conductivity	0.45	W/m/K	ISO 8302

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	< 1.0E+4	ohms·cm	IEC 60093

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	V-0		UL 94

Note Message
1 .	2.0 mm/min
2 .	2.0 mm/min

Resin Grade	Manufacturer	Category	Trademark
TOTAL Polystyrene Impact 975E	TOTAL Refining & Chemicals	PS (HIPS)	TOTAL Polystyrene
Chemlon® 60GS6	Teknor Apex Company (Chem Polymer)	Nylon 6	Chemlon®
EVERLON® TAC-50C	Ever Polymer Co., Ltd.	SEBS	EVERLON®
Fortron® 1120L4	Celanese Corporation	PPS	Fortron®
LEXAN™ HFD4211 resin	SABIC Innovative Plastics Asia Pacific	PC	LEXAN™