Ultradur® B 4300 G3
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultradur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gP0grw_Ultradur-B-4300-G3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy flowing injection molding grade with 15 % glass fibers; for rigid, tough and dimensionally stable technical parts (eg timer dials, toggles, knobs, parts for thermostats, oven-door handles, toaster housings and grills). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.40 | % | |
| Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Viscosity Number 1 | 112 | cm³/g | ISO 307 |
| Mold Shrinkage 2 | |||
| free, longitudinal | 0.50 | % | |
| free, transverse | 1.4 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Service Temperature - short cycle operation | 210 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability by Electrical Sources of Ignition - Method BH (4.00 mm) | HB | IEC 60707 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Automotive Materials (> 1.00 mm) | Pass | FMVSS 302 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 41 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ISO 75-2/A |
| Melting Temperature | 223 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 0.00120 | ||
| 1 MHz | 0.0150 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.7E-4 | ||
| 1 MHz | 3.7E-4 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| 2 . | plate with film gate 150*150*3 mm³ |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tritan™ LX500 | Eastman Chemical Company | Copolyester | Tritan™ |
| 4MID® 9A22120 | 4Plas | Nylon 66 | 4MID® |
| Celcon® M90-07 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Sylvin 8240-98FU Brown 7422 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 2990-85 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |