Hostacom G2 U02
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gOzcpT_Hostacom-G2-U02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hostacom" G2 U02 (natural) is a 20% glass coupled PP homopolymer with high flow, high stiffness, low creep under load at elevated temperatures. It is not intended for medical, pharmaceutical or drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 14 | g/10 min | |
| 230°C/5.0 kg | 55 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 230°C/2.16 kg | 16.5 | cm³/10min | |
| 230°C/5.0 kg | 66.0 | cm³/10min | |
| Molding Shrinkage | 0.20 to 1.0 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 110 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 4600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus - Secant | 4000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 160 | °C | ISO 306/A50 |
| -- | 125 | °C | ISO 306/B50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Flontech® FT-GL15-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| HONES® PPS HS-G40-3 | Guangdong Shunde Hones Polymer Material Co., Ltd. | PPS | HONES® |
| Kepital® FL2020 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Iupiace® GH30 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| CYCOLAC™ MG38N resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |