ULTEM™ 2100 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gOkA4U_ULTEM2100resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ULTEM 2100 resin is an amorphous, opaque, 10% glass fiber reinforced polyetherimide (PEI) plastic offering a glass transition temperature (Tg) of 217°C. This inherently flame retardant resin has UL94V0 and 5VA listing and is RoHS compliant. ULTEM™ 2100 resin is a glass filled general purpose grade, offering improved rigidity, high heat resistance, high strength and modulus and broad chemical resistance up to high temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 1.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.60 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 140 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 115 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 4500 | MPa | ISO 178 |
| Flexural Stress | 185 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 15.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/2C |
| Unnotched Izod Impact Strength 3 | ISO 180/1U | ||
| -30°C | 30 | kJ/m² | ISO 180/1U |
| 23°C | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 100 mm span | 210 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 205 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 223 | °C | ISO 306/A50 |
| -- | 212 | °C | ISO 306/B50 |
| -- | 217 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 150°C | 2.6E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.24 | W/m/K | ISO 8302 |
| RTI Elec | 170 | °C | UL 746 |
| RTI Imp | 170 | °C | UL 746 |
| RTI | 170 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 34 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 27 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 15 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.00 | IEC 60250 | |
| 60 Hz | 3.00 | IEC 60250 | |
| 1 MHz | 2.90 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 9.0E-4 | IEC 60250 | |
| 60 Hz | 9.0E-4 | IEC 60250 | |
| 1 MHz | 2.5E-3 | IEC 60250 | |
| 2.45 GHz | 4.6E-3 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 150 | V | IEC 60112 |
| Solution B | 100 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.410 mm | V-0 | UL 94 | |
| 1.90 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 46 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 - 120 | °C | |
| Rear Temperature | 340 - 395 | °C | |
| Middle Temperature | 350 - 405 | °C | |
| Front Temperature | 360 - 415 | °C | |
| Nozzle Temperature | 350 - 405 | °C | |
| Processing (Melt) Temp | 370 - 410 | °C | |
| Mold Temperature | 140 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra ASA HF | ResMart | ASA | ResMart Ultra |
| ALTECH® PA6 A 1000/109 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Geon™ Vinyl Flexible 90252 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| HIVOREX 2210J | Lotte Chemical Corporation | HDPE | HIVOREX |
| PHOENIX™ 16451 | Phon Tech Industrial Company | TPV | PHOENIX™ |