Laril 13 G/10-V1
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laril |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gOeEub_Laril-13-G-10-V1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Modified Polyphenylene Oxyde (PPOm) based compound. Glass fibres. UL94 V-1 classified, halogens-based flame retardants and red phosphorous free. Very high dimensional stability. Good thermal properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.55 to 0.75 | % | |
| Flow : 2.00 mm | 0.45 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 4000 | MPa | |
| 60°C | 3400 | MPa | |
| 90°C | 2800 | MPa | |
| 120°C | 2400 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 90°C | 45.0 | MPa | |
| Yield, 120°C | 20.0 | MPa | |
| Break, 23°C | 65.0 | MPa | |
| Break, 60°C | 60.0 | MPa | |
| Break, 90°C | 35.0 | MPa | |
| Break, 120°C | 15.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 90°C | 2.0 | % | |
| Yield, 120°C | 2.0 | % | |
| Break, 23°C | 3.5 | % | |
| Break, 60°C | 3.5 | % | |
| Break, 90°C | 3.8 | % | |
| Break, 120°C | 4.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 120 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 110 | °C | |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 5.0E-6 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-1 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 28 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 15 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTAMID® Care ME71 | Evonik Industries AG | PEBA-Ether | VESTAMID® Care |
| ALTECH® PP-B A 3030/500 GB30 | ALBIS PLASTIC GmbH | PP Copolymer | ALTECH® PP-B |
| CABELEC® CA4918 | Cabot Corporation | LDPE | CABELEC® |
| Ferro PP TPP40AJ35BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| SHINSTRA AG35TKB (PA6) | Shinil Chemical Industry Co., Ltd. | Nylon 6 | SHINSTRA |