Niblan VSF30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niblan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gObeGH_Niblan-VSF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT filled with 30% glass spheres for the injection moulding of items with isotropic properties |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus 1 | 4000 | MPa | ASTM D790 |
| Flexural Strength 2(Break) | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 220 | °C | ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SureSpec RP-120C | Genesis Polymers | PP Random Copolymer | SureSpec |
| alphalon™ 25 | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| Flexalloy® OR 9900-55 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| Karina CLEAR PVC COMPOUND 65/229-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PENTAMID B GV15 E H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |