Carbo-Rite™ X-5490
| Category: | PC , Polycarbonate |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Carbo-Rite™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gOZOGk_Carbo-Rite-X-5490.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Carbo-Rite™ X-5490 is a Polycarbonate compound with carbon nanotube added for enhanced electrical, mechanical and cleanliness performance. Available in pellet form for injection molding applications, Carbo-Rite™ X-5490 solves a wide range of electrostatic discharge problems. FEATURES
APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ASTM D638 |
| Tensile Strength (Break) | 52.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 17 | % | ASTM D638 |
| Flexural Modulus | 2860 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 136 | °C | |
| 1.8 MPa, Unannealed | 111 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay - 1000V to 10V | 0.1 | sec | CPM |
| Surface Resistance | < 1.0E+7 | ohms | ESD S11.11 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ionic Content 1 | Internal Method | ||
| Cl Anion | 1.00 | ng/cm² | |
| NO3 Anion | ND | ||
| SO4 Anion | 1.00 | ng/cm² | |
| Outgassing 2 | Internal Method | ||
| Acrylates | 0.00 | ng/g | |
| Styrene | 3.00 | ng/g | |
| Toluene | 16.0 | ng/g | |
| Total Outgassing | 88.0 | ng/g |
| Note Message | |
|---|---|
| 1 . | Test Method #3010-4 |
| 2 . | Test Method #3010-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E660MZAA | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| SCANLON A 5005B UV | Polykemi AB | ABS+Nylon | SCANLON A |
| Next Nylon 66 Prime Series PG40-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Karina WHITE PVC COMPOUND 803-10/34-A-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ KE002 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ STAT-KON™ |