TIPELIN® 7700M
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPELIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gOV1Vi_TIPELIN-7700M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPELIN 7700M is a natural, high density polyethylene copolymer (with butene-1 as comonomer) grade. The product shows excellent mechanical properties and environmental stress crack resistance (ESCR). The grade contains antioxidant and acid scavenger. TIPELIN 7700M is recommended for non-pressure pipes and sheet manufacturing. TIPELIN 7700M is suitable for food contact. The product complies with Food Contact Regulations. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.060 | g/10 min | |
| 190°C/21.6 kg | 8.0 | g/10 min | |
| 190°C/5.0 kg | 0.26 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, Compression Molded, F50) | > 10000 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 25.0 | MPa | |
| Break, Compression Molded | 36.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield, Compression Molded | 13 | % | |
| Break, Compression Molded | 1300 | % | |
| Flexural Modulus (Compression Molded) | 1350 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Compression Molded) | 18 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ISO 306/A120 |
| Oxidation Induction Time - Compression Molded (200°C) | > 120 | min | EN 728 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 165 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 48M10 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| Dartek O-401 | DuPont Canada, Inc. - Dartek Division | Nylon 66 | Dartek |
| Gallonprene® GP420-5503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| KOPELEN JH-370A | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| LARIPUR® LPR 8020 | COIM S.p.A. | TPU-Polyester | LARIPUR® |