Safrene® M 7650
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Safripol (PTY) LTD |
| Trademark: | Safrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gOLAm2_Safrene-M-7650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Safrene® M 7650 High Density Polyethylene Resin is a high molecular mass grade suitable for extrusion blow moulding of containers greater than 20 litre capacity. It has a high rigidity and hardness with very good impact strength and environmental stress-crack resistance properties. Safrene® M 7650 High Density Polyethylene Resin was primarily designed for the blow moulding of large hollow articles but may be used for smaller mouldings where exceptional environmental stress-crack resistance and impact strength are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.953 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 9.5 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.35 | g/10 min | ISO 1133 |
| Viscosity Number (Reduced Viscosity) | 350.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, molding | 26.0 | MPa | ISO 527-2/50 |
| Fracture, molding | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, Compression Molded) | > 600 | % | ISO 527-2/50 |
| Flexural Stress (3.5% Strain, Compression Molded) | 22.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C, molded | 20 | kJ/m² | ISO 179 |
| 23°C, molded | 23 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 80.0 | °C | ISO 306/B |
| Peak Crystallization Temperature (DSC) | 130 - 133 | °C | ISO 3146 |
| Additional Information |
|---|
| Blow Molding conditions: Feed Zone: 180°C Zone 1: 190 to 200°C Zone 2: 200 to 210°C Zone 3: 200°C Die: 200°C Melt Temperature: 200°C |
| Note Message | |
|---|---|
| 1 . | Unannealed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRP9619A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Sindustris PP M1426 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Badamid® LB70 L | Bada AG | Nylon 6 | Badamid® |
| Sylvin 9077-94 Grey 9529 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ RCL36S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |