POLYFORT® FPP 20 GFC LE K1400
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFORT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gOENX5_POLYFORT-FPP-20-GFC-LE-K1400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% glass fibre reinforced PP Homopolymer chemically coupled, high heat stabilized, low emission |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 10.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 106 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 69.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.8 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 23 | kJ/m² | ISO 179/1eU |
| 23°C | 43 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 156 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 129 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 164 | °C | ISO 306/A50 |
| -- | 126 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | mm/min | ISO 3795 |
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HG3101 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Hanwha Total TPE SE80 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | TPE | Hanwha Total TPE |
| Karina WHITE PVC COMPOUND TR-600-10/125-G-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TechnoFin PP EPDM T 20 | TechnoCompound GmbH | PP+EPDM | TechnoFin |
| LEXAN™ 203R resin | SABIC Innovative Plastics | PC | LEXAN™ |