Starex NA-0660I
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gO89XR_Starex-NA-0660I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS material with the characteristic of nano-silver high flowability antibacterial ABS that can be applied to notebook keyboard |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 1 | 39.0 | MPa | ASTM D638 |
| Yield | 40.0 | MPa | ISO 527-2/50 |
| Break | 33.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | 30 | % | ASTM D638 |
| Break | 15 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 3 | 2200 | MPa | ASTM D790 |
| -- 4 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 5 | 59.0 | MPa | ASTM D790 |
| -- 6 | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 23 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 340 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 220 | J/m | ASTM D256 |
| 23°C 8 | 22 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 93.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 102 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 82.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 82.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 98.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 97.0 | °C | ISO 306/B50 |
| -- | 101 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 210 to 220 | °C | |
| Nozzle Temperature | 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 147 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Thickness: 4 mm |
| 8 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Diamond Plastics Laser HDPE HX 17 | Diamond Plastics GmbH | TP, Unspecified | Diamond Plastics |
| Ecobarrier® 0714 | Noble Polymers | Polyolefin, Unspecified | Ecobarrier® |
| Elastollan® 1185A10 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| ENVIROPLAS® ENV11-NC720 | ENVIROPLAS®, Inc. | PC | ENVIROPLAS® |
| Petrotene® PP A3 T20 HF NTLA010 PH370 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |