NORYL™ WCA955 resin
| Category: | PPE+TPE , Polyphenylene Ether + TPE |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gNNYFa_NORYL-WCA955-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non-halogenated flame retardant Flexible NORYL extrusion grade intended for evaluation in wire insulation, especially for internal wire. Excellent flame retardant performance with balanced tensile strength, tensile elongation, heat deformation, capable of VW-1 performance and 105C temperature rating as defined by UL 1581. Processing typically conducted on standard extrusion equipment. UL 1581 tests conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor. It"s also suitable for coating of AWG26 and AWG28 copper conductor as well. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 30 sec) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture | 27.0 | MPa | UL 1581 |
| Fracture 1 | 15.0 | MPa | ASTM D638 |
| Fracture, 136°C 2 | 27.0 | MPa | UL 1581 |
| Fracture | 15.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture | 250 | % | UL 1581 |
| Fracture 3 | 160 | % | ASTM D638 |
| Fracture, 136°C 4 | 180 | % | UL 1581 |
| Fracture | 160 | % | ISO 527-2/50 |
| Flexural Modulus 5 | |||
| 100mm span | 150 | MPa | ASTM D790 |
| -- | 140 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UL Temperature Rating | 105 | °C | UL 1581 |
| Heat Deformation 6(121°C) | 4.0 | % | UL 1581 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| VW-1 | Pass | UL 1581 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.4E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (3.00 mm) | 750 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 725 | °C | IEC 60695-2-13 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 5.0 - 7.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 220 - 250 | °C | |
| Cylinder Zone 5 Temp. | 220 - 250 | °C | |
| Melt Temperature | 220 - 250 | °C | |
| Die Temperature | 220 - 250 | °C |
| Extrusion instructions |
|---|
| Conductor Pre-heat Temperature: 25 - 120 °CCooling Water Air Gap: 100 - 200 mmCross-head Temperature: 220 - 250 °CDrying Time (Cumulative): 12 hrsExtruder Length/Diameter Ratio (L/D): 22:1 to 26:1Neck Temperature: 220 - 250 °CScreen Pack: 150 - 100Screw Speed: 15 - 85 rpmWater Bath Temperature: 15 - 60 °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | After 7 days |
| 3 . | Type 1, 50mm/min |
| 4 . | After 7 days |
| 5 . | 13 mm/min |
| 6 . | 250 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 7105D | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| Shandong PA6 GFPA630-3 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6 | Shandong PA6 |
| LGSTRENE LGS GZ12 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGSTRENE |
| Integra™ PC-5025 R 0002 | PolySource, LLC | PC | Integra™ |
| apilon 52® TL 72 | API SpA | TPU-Polyether | apilon 52® |