Braskem EVA TN2005
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem EVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gNER4u_Braskem-EVA-TN2005.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TN2005 is an Ethylene-Vinyl Acetate (EVA) copolymer with high molecular weight, excellent mechanical properties, transparency, high gloss and easy processability. Additionally, TN2005 has flexibility even at low temperatures and good sealing properties. TN2005 can be used as base polymer for the manufacture of greenhouse films with excellent thermal properties. More detailed information about agricultural film applications and light stabilization recommendations, please contact a Braskem representative. Application:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 13.5 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, Compression Molded | 91 | ||
| Shore D, Compression Molded | 50 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 25.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 680 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 50 µm, Blown Film | 60.0 | MPa | |
| 2% Secant, TD : 50 µm, Blown Film | 70.0 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 30.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 34.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 400 | % | |
| TD : Break, 50 µm, Blown Film | 800 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 430 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, Blown Film | 100 | g | |
| TD : 50 µm, Blown Film | 270 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 75.0 | °C | ASTM D1525 1 |
| Peak Melting Temperature | 94.0 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 82 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 2.2 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 145 to 185 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PS 3122 (UK) | MBA Polymers | PS (GPPS) | MBA PS |
| ExxonMobil™ HDPE HD 7960.13 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| HYBRANCH XC-540 HB | DIC Corporation | PS (Specialty) | HYBRANCH |
| Ducor® 1040TC | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| LNP™ THERMOCOMP™ MFB71L compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |