Category: | EVA , Ethylene Vinyl Acetate Copolymer Resin |
Manufacturer: | ExxonMobil Chemical |
Trademark: | Escorene™ Ultra |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | gMdP0U_Escorene-Ultra-UL-00112.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
UL 00112 is a copolymer of ethylene and vinyl acetate. |
General Information |
---|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
Vinyl Acetate Content | 12.0 | wt% | ExxonMobil Method |
Films | Nominal Value | Unit | Test Method |
---|---|---|---|
secant modulus | ASTM D882 | ||
1% secant, MD | 100 | MPa | ASTM D882 |
1% secant, TD | 110 | MPa | ASTM D882 |
Tensile Strength | ASTM D882 | ||
MD : Fracture | 30.0 | MPa | ASTM D882 |
TD : Fracture | 29.0 | MPa | ASTM D882 |
Tensile Elongation | ASTM D882 | ||
MD : Fracture | 590 | % | ASTM D882 |
TD : Fracture | 620 | % | ASTM D882 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Vicat Softening Temperature | 75.0 | °C | ASTM D1525 |
Legal statement |
---|
有关潜在食品接触应用合规信息(例如:FDA、EU、HPFB),请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用,亦不应在任何此类应用中使用 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
MarFlex® 5429 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
SHIN-A SE-55A | SHIN-A T&C | Epoxy | SHIN-A |
SUPREME HIPS SH825 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
ESTASTIR HI 0408 V0 | Cossa Polimeri S.r.l. | PS (HIPS) | ESTASTIR |
Hostacom HBG H01 NAT | LyondellBasell Industries | PP Homopolymer | Hostacom |