GLS Nylon 66 LN06
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS Nylon 66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gMGzd9_GLS-Nylon-66-LN06.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nylon66 FR V0 Precolor |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 to 1.26 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.2 to 1.8 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 65.0 to 70.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus 3 | 3500 to 4000 | MPa | ASTM D790 |
| Flexural Strength 4 | 115 to 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 35 to 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 67.0 to 70.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 55.0 to 95.0 | °C | |
| Injection Pressure | 70.0 to 105 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VDM93-15E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Terblend® N NG-04 | INEOS Styrolution Group GmbH | ABS+Nylon | Terblend® N |
| Fortron® 6850L6 | Celanese Corporation | PPS | Fortron® |
| Orgalloy® LE 60LM | Arkema | Nylon 6 Alloy | Orgalloy® |
| PERLER® O08U1000B10 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |