Resinoid 2089
| Category: | Phenolic , Phenolic |
| Manufacturer: | Resinoid Engineering Corporation |
| Trademark: | Resinoid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gM6u68_Resinoid-2089.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Resinoid 2089 is a chopped fabric reinforced, two-step phenolic molding compound offering good physical and wear properties. This product has been specifically formulated for mechanical applications where minimal wear and low shrinkage values are desired. This material comes in bulk fabric form and is suitable for compression molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792A, ISO 1183 |
| Molding Shrinkage - Flow | 0.15 | % | ASTM D955, ISO 294-4 |
| Water Absorption | |||
| 24 hr | 0.80 | % | ASTM D570 |
| 23°C, 24 hr | 0.80 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | |||
| -- | 8270 | MPa | ASTM D790 |
| -- | 8200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 68.9 | MPa | ASTM D790 |
| -- | 69.3 | MPa | ISO 178 |
| Compressive Strength | 110 | MPa | ASTM D695, ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 130 | J/m | ASTM D256A |
| -- | 13 | kJ/m² | ISO 180/2A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx CPP5B10 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| Sanren N110 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| RTP 101 SP (20% FOAMED) | RTP Company | PP, Unspecified | RTP |
| Taitalac® 1003 | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| ACCUTECH™ CP0437M40L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |