Bergamid™ A70 G50 H Natural
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gLn6GT_Bergamid-A70-G50-H-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bergamid A70 G50 H Natural is a Polyamide 66 (Nylon 66) product filled with 50% glass fiber. It can be processed by injection molding and it is heat stabilized. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 16500 | MPa | ISO 527-2 |
| Tensile Strength | 230 | MPa | ISO 527 |
| Tensile Strain (Break) | 2.0 | % | ISO 527 |
| Flexural Strength | 305 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 95 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Continuous Use Temperature | 130 | °C | IEC 216 |
| Melting Temperature (DSC) | 255 to 265 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 90 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | IEC 60250 | |
| Dissipation Factor | 0.030 | IEC 60250 | |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Flexible 7072 NAT | Prime PVC® | PVC, Flexible | Prime Flexible |
| YUPLENE® H350F | SK Global Chemical | PP Homopolymer | YUPLENE® |
| LEXAN™ FXEMPX2 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Braskem PP F013M | Braskem America Inc. | PP Homopolymer | Braskem PP |
| LNP™ THERMOCOMP™ DB008ERP compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |