TEKALOY™ G70A3
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gL6Fx4_TEKALOY-G70A3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| G70A3 is a PC/ABS alloy unreinforced with heat resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 57.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | > 100 | % | ASTM D638 |
| Flexural Modulus 3 | 2160 | MPa | ASTM D790 |
| Flexural Strength 4 | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 115 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 220 to 280 | °C | |
| Middle Temperature | 220 to 280 | °C | |
| Front Temperature | 220 to 280 | °C | |
| Nozzle Temperature | 230 to 290 | °C | |
| Processing (Melt) Temp | 220 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT2500-01A | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Tenite™ Propionate 383A2R30007 Natural, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| VITAMIDE® BI14 | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| Unilex™ UP 8034NW | United Polychem | PP Homopolymer | Unilex™ |
| Karina BLACK PVC COMPOUND TR-105850-48/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |