TAROLOY 50
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gKkUPu_TAROLOY-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAROLOY 50 is a Polycarbonate + PBT (PC+PBT) product. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.80 to 1.1 | % | |
| Flow | 0.80 to 1.1 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.10 | % | |
| Saturation, 23°C | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 55.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Strain (Break) | 120 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Flexural Stress 2 | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 600 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 90.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 3 | 90.0 | °C | IEC 60216 |
| Vicat Softening Temperature | 170 | °C | ISO 306/A50 |
| Ball Pressure Test (135°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (-30 to 30°C) | 9.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (3.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 110 | °C | |
| Pre-heater | 110 to 120 | °C | |
| Drying Time | |||
| -- | 2.0 | hr | |
| Pre-heater | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | 20000 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9077-92 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VESTODUR® 1003-FR3 | Evonik Industries AG | PBT | VESTODUR® |
| DEXFLEX® 727 FP BLK | LyondellBasell Industries | TPO (POE) | DEXFLEX® |
| FRblend® PP-1309 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP, Unspecified | FRblend® |
| Ketron® PEEK-CA30 | Quadrant Engineering Plastic Products | PEEK | Ketron® |