PENTAMID B S L H natural
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gKgPb6_PENTAMIDBSLHnatural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low viscosity, impact modified, heat stabilised polyamide 6 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.20 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 2.1 | -- | % | ISO 294-4 |
| Flow | 1.7 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 9.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.6 | -- | % | ISO 62 |
| Viscosity Number | 130 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2600 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 71.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.4 | 13 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 170 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 223 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.6 mm | HB | -- | UL 94 | |
| 3.2 mm | HB | -- | UL 94 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA6-I, MHR, 12-020 | -- | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 70 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.10 - 0.18 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 255 - 275 | °C | |
| Middle Temperature | 260 - 285 | °C | |
| Front Temperature | 265 - 275 | °C | |
| Processing (Melt) Temp | 250 - 290 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 55.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer FEA-241U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| TAROPRENE® 1 A30 M1M | Taro Plast S.p.A. | TPV | TAROPRENE® |
| THERMOLAST® K TF6FMA (Series: FC/AD1) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Xuchuan XCW-30BA-6B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Dryflex® SE 60A301N U | ELASTO | SEBS | Dryflex® |