Celstran® PP-GF20-02 Natural
| Category: | PP Homopolymer , Polypropylene |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celstran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gKeWXl_Celstran-PP-GF20-02-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% long glass polypropylene developed for aesthetic applications requireing good impact with a class A appearance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.70 | % | ISO 294-4 |
| Flow direction | 0.47 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5390 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 111 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.9 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 5100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 157 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 220 - 230 | °C | |
| Middle Temperature | 230 - 240 | °C | |
| Front Temperature | 240 - 250 | °C | |
| Nozzle Temperature | 240 - 250 | °C | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 30.0 - 70.0 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Feed Temperature: 20 to 50°CZone 4 Temperature: 250°CManifold Temperature: 230 to 270°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® 1011R BRIGHT | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |
| Ultramid® B3EG3 | BASF Corporation | Nylon 6 | Ultramid® |
| VALOX™ 420 resin | SABIC Innovative Plastics | PBT | VALOX™ |
| Ateva® 2825A | Celanese EVA Performance Polymers | EVA | Ateva® |
| Axiall PVC 8805 | Axiall Corporation | PVC, Flexible | Axiall PVC |