EL-Lene™ H455JA
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Lene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gK0wSF_EL-Lene-H455JA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Lene H455JA is a high density polyethylene resin with narrow molecular weight distribution, good processing performance, organoleptic property. It is particularly designed for injection molding and extrusion compression molding of screw cap and closure. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.961 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | TPE | ||
| Flow : 2.00 mm | 2.1 | % | |
| Across Flow : 2.00 mm | 2.1 | % | |
| Environmental Stress-Cracking Resistance (50°C, 10% Igepal, Compression Molded, F50) | 7.00 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 27.5 | MPa | |
| Break | 250 | MPa | |
| Tensile Elongation 2(Break) | 1300 | % | ASTM D638 |
| Flexural Modulus | 1230 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 84.0 | °C | ASTM D648 |
| Brittleness Temperature | -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Peak Melting Temperature | 132 | °C | ASTM D2117 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 240 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WACKER® PRIMER G 718 | Wacker Chemie AG | Silicone | WACKER® |
| Axiall PVC 10757 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Cereplast Compostables® 2001 | Cereplast, Inc. | PLA | Cereplast Compostables® |
| Elastamax™ XL-2185 | PolyOne Corporation | TPO (POE) | Elastamax™ |
| KEBAFLEX® E 50.1 | BARLOG plastics GmbH | TPV | KEBAFLEX® |