Somos® NeXt
| Category: | Unspecified , Unspecified |
| Manufacturer: | DSM Somos® |
| Trademark: | Somos® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gIpwQZ_Somos-NeXt.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Somos® NeXt is an extremely durable stereolithography (SL) resin that produces very accurate parts with high feature detail. Based on the Somos® DMX technology, Somos® NeXt is a next generation of material that facilitates the production of tough, complex parts with improved moisture resistance and greater thermal properties. Applications Somos® NeXt produces parts that are much more resistant to breakage than parts made with standard SL resins. It is ideal for use in functional testing applications as well as low-volume manufacturing applications where toughness is required. Market segments include aerospace, automotive, medical, consumer products and electronics. This resin is ideal for functional end-use performance prototypes such as: snap- fit designs, impellers, duct work, connectors and electronic covers, automotive housings and dashboard assemblies, packaging and sporting goods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | |
| Water Absorption (Equilibrium) | 0.39 to 0.41 | % | ASTM D570 |
| Viscosity (30°C) | 1.00 | Pa·s |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Critical Exposure | 12.0 | mJ/cm² | |
| Penetration Depth | 147.3 | µm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2370 to 2490 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 41.1 to 43.3 | MPa | |
| Break | 31.0 to 34.6 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.0 | % | |
| Break | 8.0 to 10 | % | |
| Flexural Modulus | 2420 to 2530 | MPa | ASTM D790 |
| Flexural Strength | 67.8 to 70.8 | MPa | ASTM D790 |
| Poisson's Ratio | 0.42 to 0.44 | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 47 to 52 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 55.0 to 57.0 | °C | |
| 1.8 MPa, Unannealed | 48.0 to 51.0 | °C | |
| Glass Transition Temperature | 43.0 to 47.0 | °C | ASTM E1545 |
| CLTE - Flow | ASTM E831 | ||
| -40 to 0°C | 7.2E-4 to 7.4E-4 | cm/cm/°C | |
| 0 to 50°C | 1.1E-3 | cm/cm/°C | |
| 50 to 100°C | 1.7E-3 to 1.8E-3 | cm/cm/°C | |
| 100 to 150°C | 1.7E-3 to 1.8E-3 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 15 to 16 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 4.65 | ||
| 1 kHz | 3.97 | ||
| 1 MHz | 3.62 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 SI 2 DEL | RTP Company | Acetal (POM) Copolymer | RTP |
| MIDILENA III HDPERBI 8.0 | ROMPETROL PETROCHEMICALS S.R.L. | HDPE | MIDILENA III |
| SLOVASTER® B1 GF 45 | Plastcom | PBT | SLOVASTER® |
| Hostacom X M2 V05 C11323 | LyondellBasell Industries | PP Copolymer | Hostacom |
| SABIC® LLDPE 6135BE | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |