SABIC® HDPE B5429
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gHx2ot_SABIC-HDPE-B5429.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE B5429 is a medium molecular weight high density polyethylene copolymer. It is typically used for blow moulding bottles of small sizes. SABIC® HDPE B5429 offers a very good combination of toughness, stress cracking resistance (ESCR), load bearing strength and processability characteristics. Typical applications. SABIC® HDPE B5429 is classified as a multipurpose blow moulding grade. It may be blow moulded into containers for household and industrial chemicals (e.g. detergents, bleach, fabric softeners, solvents, paints, etc.), automotive supplies, foodstuffs, toiletries and cosmetics. It is typically also used for other hollow thin-walled parts and profile extrusions. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.30 | g/10 min | |
| 190°C/21.6 kg | 29 | g/10 min | |
| 190°C/5.0 kg | 1.5 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Igepal CO-630, Compression Molded, F50) | 40.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 61 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1050 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress | ISO 527-2/1BA/50 | ||
| Yield, 2.00 mm, Compression Molded | 26.0 | MPa | |
| Break, 2.00 mm, Compression Molded | 28.0 | MPa | |
| Tensile Strain (Break, 2.00 mm, Compression Molded) | > 1000 | % | ISO 527-2/1BA/50 |
| Flexural Modulus (2.00 mm, Compression Molded) | 1250 | MPa | ISO 178 |
| Flexural Stress (2.00 mm, Compression Molded) | 27.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Compression Molded | 5.0 | kJ/m² | |
| 23°C, Compression Molded | 12 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 81.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 1 |
| Melting Temperature | 132 | °C | DIN 53765 |
| Enthalpy Change | 205 | J/g | DIN 53765 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Melt Temperature | 165 to 215 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Appeel® 11D888 | DuPont Packaging & Industrial Polymers | EVA | Appeel® |
| Hiprolon® 400 NN | Arkema | Nylon 1012 | Hiprolon® |
| LNP™ LUBRICOMP™ KA000 compound | SABIC Innovative Plastics Europe | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| OmniLon™ PA6 U GR33 BK1000 | OMNI Plastics, LLC | Nylon 6 | OmniLon™ |
| TechnoFin PP T 22 | TechnoCompound GmbH | PP, Unspecified | TechnoFin |