SABIC® PPcompound 7727
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gHqWvW_SABIC-PPcompound-7727.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND 7727 is a mineral filled, impact modified polypropylene TPO. This material combines impact resistance, heat stability, and is used in injection molded applications. The IMDS ID is 209708556. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.998 | g/cm³ | ASTM D792 |
| -- | 0.990 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1960 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 25.0 | MPa | ISO 527-2/50 |
| Break | 18.3 | MPa | ISO 527-2/1A/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 4.6 | % | |
| Break | 27 | % | |
| Flexural Modulus 1(64.0 mm Span) | 2060 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 4.6 | kJ/m² | ISO 179/1eA |
| Instrumented Dart Impact 3(23°C, Energy at Peak Load) | 21.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed | 114 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 62.7 | °C | ISO 75-2/A |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 56.4 | µm/Mk | |
| Transverse : -30 to 100°C | 116 | µm/Mk |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 250 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 mm, Cut |
| 3 . | 6.60 m/sec |
| 4 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech B9000EX | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 6 | Sup-tech |
| Nypol® PA A3 T40 HL CNZA0040 NR359 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| ColorRx® PP2-0900RX | LTL Color Compounders, Inc. | PP Random Copolymer | ColorRx® |
| Geon™ Vinyl Rigid Extrusion L0152 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Silastic® Q7-4850 | Dow Corning Corporation | Silicone | Silastic® |