RTP 283H L
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gHbGkB_RTP-283H-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13800 | MPa | ASTM D638 |
| Tensile Strength | 145 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus | 10300 | MPa | ASTM D790 |
| Flexural Strength | 214 | MPa | ASTM D790 |
| Compressive Strength | 131 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 190 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 910 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 257 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 249 | °C | ASTM D648 |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.69 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+2 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 3mil/in.Tensile Elongation, ASTM D-638: 3-4% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 274 - 288 | °C | |
| Middle Temperature | 274 - 288 | °C | |
| Front Temperature | 274 - 288 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spectar™ Copolyester 14471 | Eastman Chemical Company | Copolyester | Spectar™ |
| AEI SX409:CM401 | AEI Compounds Limited | LDPE | AEI |
| Badamid® A70 GK15 TM-Z3 | Bada AG | Nylon 66 | Badamid® |
| Hipolyene 3152 MC | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Plaslube® ABS/PBT GF20 | Techmer Engineered Solutions | ABS+PBT | Plaslube® |