TOTAL Polystyrene 814
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGzCzE_TOTAL-Polystyrene-814.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polystyrene Compound 814 is a high heat resistant, V0 brominated flame retardant, high impact polystyrene for injection molding application. It is recommended for manufacturing of articles which require good dimensional stability. Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.5 | g/10 min | ASTM D1238 |
| Spiral Flow 1 | 47.0 | cm | ASTM D3123 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | < 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C, Injection Molded) | 93 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, Injection Molded) | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C, Injection Molded) | 40 | % | ASTM D638 |
| Flexural Modulus (23°C, Injection Molded) | 2100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.0 | °C | ASTM D1525 2 |
| CLTE - Flow | 8.9E-5 | cm/cm/°C | ASTM D696 |
| Heat Distortion | 77 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Dielectric Strength | 160 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | UL 94 | |
| 2.50 mm | 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 160 - 180 | °C | |
| Middle Temperature | 180 - 200 | °C | |
| Front Temperature | 190 - 210 | °C | |
| Nozzle Temperature | 210 - 230 | °C |
| Injection instructions |
|---|
| Zone 4 Temperature: 200 to 220°C |
| Note Message | |
|---|---|
| 1 . | Mold temperature: 220°C |
| 2 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ALC-90A-B30 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| Gallonprene® GP520-5012 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LUVOCOM® 1105-7336/GY7016 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| LUVOCOM® 1105-7185 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| LUVOCOM® 1500-0871 | LEHVOSS Group | PSU | LUVOCOM® |