ENVIRON® ENV39-NC450
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIRON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGrlLp_ENVIRON-ENV39-NC450.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, Flame Retardant, Impact-Modified, RoHS Compliant NC450 = To Be Assigned 5 Digit Number Indicating Natural, Black, or Limited Available Custom Color. The ENV39 Series Products Are Available With Mold Release and/or UV Stabilizer. Contact Enviroplas Regarding UL Recognized Versions Of This Product. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 50.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus | 2100 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 450 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 96.1 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | Internal Method | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 235 to 249 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 246 to 266 | °C | |
| Nozzle Temperature | 246 to 260 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Beamset 371 | Arakawa Chemical Industries, Ltd. | Epoxy | Beamset |
| Ferro PP TPP20AN50WH | Ferro Corporation | PP, Unspecified | Ferro PP |
| KOPA® KN333G33CR | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Jiangsu Sinarise PX901X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Neoplast™ 167 HOFR | Zylog Plastalloys Pvt. Ltd. | TPV | Neoplast™ |