TOPAS® 8007F-500
| Category: | COC , Cyclic Olefin Copolymer |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | TOPAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGgFaO_TOPAS-8007F-500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Film grade, Improved moldability |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 2.00 | cm³/10min | |
| 230°C/2.16 kg | 11.0 | cm³/10min | |
| Water Absorption (Saturation, 23°C) | 0.010 | % | ISO 62 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD | 2100 | MPa | |
| TD | 1800 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break | 55.0 | MPa | |
| TD : Break | 52.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break | 3.4 | % | |
| TD : Break | 3.4 | % | |
| Water Vapor Transmission Rate (38°C, 90% RH) | 0.085 | g·mm/m²/atm/24 hr | ISO 15106-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 1 | 78.0 | °C | ISO 11357-2 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 4018 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| SynPlast™ NOTM-E | PolyOne Corporation | Tri (n-octyl) Trimellitate | SynPlast™ |
| ALCOM® PC + ABS 750/8 PTFE8 | ALBIS PLASTIC GmbH | PC+ABS | ALCOM® PC + ABS |
| Hyundai EP PA66 LD630 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| Sylvin 9077-92 Blue 8224 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |