Capilene® G 65 F
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGgEEt_Capilene-G-65-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CAPILENE ® G 65 F is a polypropylene homopolymer intended for biaxially oriented polypropylene (BOPP) film applications. CAPILENE ® G 65 F features: good processability, easy film stretchability and good mechanical properties; does not contain calcium stearate, slip and anti-blocking additives. CAPILENE ® G 65 F is suitable for: BOPP plain or coextruded packaging films, metallizable BOPP film; extrusion and coextrusion thermoforming. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 33.0 | MPa | ASTM D638 |
| Yield | 30.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 15 | % | ASTM D638 |
| Yield | 13 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 1550 | MPa | ASTM D790 |
| -- 3 | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 40 | J/m | ASTM D256 |
| 23°C | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 89.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 155 | °C | ISO 306/A, ASTM D1525 4 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 126F5 | SAX Polymers | Nylon 6 | SAXAMID™ |
| TRIBOCOMP® PA6 TS0 | EPIC Polymers | Nylon 6 | TRIBOCOMP® |
| Ferro PP TPP20AF70UL | Ferro Corporation | PP Homopolymer | Ferro PP |
| Sylvin 8280-85UV White 1549 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Plexar® PX2600 | LyondellBasell Industries | PE, Unspecified | Plexar® |