Akoafloor PB R 509 brown
| Category: | PB , Polybutylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Akoafloor |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGb9xK_Akoafloor-PB-R-509-brown.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akoafloor PB R 509 brown is a highly isotactic random copolymer manufactured from butene-1 monomer. The product provides good long term hydrostatic strength also at elevated temperatures combined with extremely high flexibility. Akoalit PB R 509 complies with requirements specified in ISO 12230, DIN 16968/DIN 16969 for PB-1 pipe applications. The grade is typically used for under floor heating or surface cooling applications. Akoalit PB R 509 is available in brown colour in pellet form. Akoalit PB R 509 is not being sold for pipe applications in North America. The grade is not intended for medical or pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 8986-2 | ||
| Yield, molding | 18.0 | MPa | ISO 8986-2 |
| Fracture, molding | 38.0 | MPa | ISO 8986-2 |
| Tensile Strain 2(Break, Compression Molded) | 330 | % | ISO 8986-2 |
| Flexural Modulus | 330 | MPa | ISO 178 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 240 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 175 - 190 | °C |
| Extrusion instructions |
|---|
| Vacuum: 30 mbar to 60 mbarCooling Water Temperature: 10 to 12°C |
| Note Message | |
|---|---|
| 1 . | Type IV, Conditioned 10 days at 20°C |
| 2 . | Type IV, Conditioned 10 days at 20°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 216 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| ACRYPET® IR G504 | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | ACRYPET® |
| Gallonprene® GP310-9001 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Karina CLEAR PVC COMPOUND -E 70/222-D-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| NORYL™ SE1X resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |