LNP™ LUBRICOMP™ WX07423H compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGQ5wK_LNP-LUBRICOMP-WX07423H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Health care grade, PTFE and silicone lubricated Also known as: LNP* LUBRICOMP* Compound PDX-W-07423 HC Product reorder name: WX07423H |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 62 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.6 to 2.8 | % | |
| Across Flow : 24 hr | 2.5 to 2.7 | % | |
| Water Absorption (24 hr, 50% RH) | 0.075 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2550 | MPa | ASTM D638 |
| -- | 2680 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 43.5 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2/5 |
| Break 3 | 43.0 | MPa | ASTM D638 |
| Break | 45.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 11 | % | ASTM D638 |
| Yield | 18 | % | ISO 527-2/5 |
| Break 5 | 14 | % | ASTM D638 |
| Break | 19 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2300 | MPa | ASTM D790 |
| -- 7 | 2400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 74.5 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 74.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.33 | ||
| vs. Itself - Static | 0.24 | ||
| Wear Factor - Washer | 5.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 30 | J/m | ASTM D256 |
| 23°C 9 | 4.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D4812 |
| 23°C 10 | 44 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 55.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecomid® NA40 GR50 NL RM | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| TECHNYL® A 31T1 MZ40 GREY 174 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Sindustris PC GP1001MD | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| G-PAEK™ 1120FE | Gharda Chemicals Ltd. | PEK | G-PAEK™ |
| Karina GRAY PVC COMPOUND -E 854-18/ 99-CRB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |