ALCUDIA® HDPE T-100-N
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGKBtT_ALCUDIA-HDPE-T-100-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® T-100-N black compound is a high density polyethylene with a broad bimodal molecular weight distribution, especially apt for the extrusion of pipe for potable water and natural gas, to comply with the requirements of prEN 12201 and prEN 1555 European specification standards. The combination of the antioxidant system and minimum of 2.0% well dispersed carbon black used in T-100-N provides the following features:
Based on the UNE EN 12201 and UNE EN 1555 classification the ALCUDIA® T-100-N compound is classified as PE100. Because other good mechanical properties and their characteristics, the polyethylene black compound ALCUDIA® T-100-N, is designed to produce large diameter pipe for potable water and fittings and valves for the transport of water. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.10 | g/10 min | |
| 190°C/5.0 kg | 0.40 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Antarox CO-630, F50) | > 10000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 23°C) | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 600 | % | ISO 527-2 |
| Internal Pressure Resistance | EN 1555/12201 | ||
| 10 MPa : 20°C | > 4.2 | day | |
| 4.0 MPa : 80°C | > 41.7 | day | |
| 4.6 MPa : 80°C | > 6.9 | day | |
| Resistance to Rapid Crack Propagation, Pc (0°C) 1 | > 10.0 | bar | ISO 13477 |
| Resistance to Slow Crack Growth (80°C) 2 | 500 | hr | ISO 13479 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | > 20 | min | EN 728 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Long-Term Hydrostatic Strength - 50 years (20°C) 3 | 10.0 | MPa | ISO TR 9080 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 119 | °C | ISO 306/A50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 175 to 195 | °C | |
| Cylinder Zone 2 Temp. | 180 to 200 | °C | |
| Cylinder Zone 3 Temp. | 185 to 205 | °C | |
| Cylinder Zone 4 Temp. | 190 to 210 | °C | |
| Cylinder Zone 5 Temp. | 195 to 215 | °C | |
| Melt Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 110x15 mm pipe, S4 Test |
| 2 . | 9.2 bar |
| 3 . | Regression Curve |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ColorRx® PCPT-0900CRNB | LTL Color Compounders, Inc. | PC+PET | ColorRx® |
| Crastin® SK692FR BK507 | DuPont Performance Polymers | PBT | Crastin® |
| Karina COMP. PVC IVORY -E 600D35/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lumid® GP2251BF | LG Chem Ltd. | Nylon 66 | Lumid® |
| O'Tech OM 6737 | O'Tech Corporation | PVC, Unspecified | O'Tech |