EMAREX® 400 GF43
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | MRC Polymers, Inc. |
| Trademark: | EMAREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gGCDSK_EMAREX-400-GF43.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Further information and details are available upon request.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.0 | % | ASTM D570 |
| Relative Viscosity | 50 | mPa·s | ASTM D789 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 103 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 215 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus - Tangent | 11000 | MPa | ASTM D790 |
| Flexural Strength | 296 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 260 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 252 | °C | ASTM D648 |
| Melting Temperature | 265 | °C | ASTM D789 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Dew Point | < -17.8 | °C | |
| Suggested Max Moisture | 0.14 | % | |
| Rear Temperature | 288 - 299 | °C | |
| Middle Temperature | 277 - 282 | °C | |
| Front Temperature | 271 - 277 | °C | |
| Nozzle Temperature | 282 - 293 | °C | |
| Processing (Melt) Temp | 271 - 293 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa | |
| Screw Speed | 30 - 90 | rpm | |
| Cushion | 6.35 | mm |
| Injection instructions |
|---|
| Packing: 50 to 75% of injection pressureHold: 40 to 60% of injection pressureAir Flow Rate: 0.8-1.0 CFM per lb/hour resin processed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6 7500 GF30 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Verolloy B6726 | PlastxWorld Inc. | ABS+PBT | Verolloy |
| Chemlon® 225 G | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Karina GREEN PVC COMPOUND 861-40/36-IS-RG (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ RAL22S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |