DOMAMID® 66G35V0P 1001
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | DOMO Engineering Plastics SPA |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gG4UK9_DOMAMID-66G35V0P-1001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, 35% glass fiber reinforced, red phosphorous flame retardant, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 2577 | ||
| Across Flow : 23°C, 72 hr | 0.80 to 1.0 | % | |
| Flow : 23°C, 72 hr | 0.30 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 160 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 9000 | MPa | ISO 178 |
| Flexural Stress 3 | 205 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 65 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 250 | °C | ISO 306/B50 |
| Melting Temperature | 263 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 575 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (1.00 to 3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 to 3.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Europrene® HS 630 | Versalis S.p.A. | SBR, Emulsion | Europrene® |
| Hanwha Total PP KH52T | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| OmniPro™ CPP CCF40 | OMNI Plastics, LLC | PP Copolymer | OmniPro™ |
| ESTOPLAST XU 215BB10 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |
| DAI-EL™ G-7201 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |