ASTALAC™ ABS X15P
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gG2rbB_ASTALAC-ABS-X15P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTALAC™ ABS X15P is a high heat resistance grade of ABS which is designed for highly decorated injection moulding applications requiring a balance of heat resistance, impact toughness, product rigidity and mouldability. Typical automotive applications include interior decorative and functional components such as console assemblies, spears and switchplates. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 7.0 | g/10 min | |
| 230°C/3.8 kg | 2.0 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 44.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 35 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2300 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 72.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 85.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 92.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 100 | °C | |
| Vicat Softening Temperature | 115 | °C | ASTM D1525 5 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 95.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 215 to 235 | °C | |
| Middle Temperature | 225 to 245 | °C | |
| Front Temperature | 235 to 255 | °C | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 TFE 10 SI | RTP Company | Nylon 66 | RTP |
| Cheng Yu ML3435 | Cheng Yu Plastic Company Limited | PC | Cheng Yu |
| PEARLCOAT® 125K | Lubrizol Advanced Materials, Inc. | TPU-Polyester | PEARLCOAT® |
| Plexiglas® LED 8N LD96 | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| Sylvin 83052-90 White 1592 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |