SCHULAKETON GF 30
| Category: | PK-Aliphatic , Polyketone, Aliphatic |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAKETON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gFmhew_SCHULAKETON-GF-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber reinforced aliphatic Polyketon |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (240°C/2.16 kg) | 6.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 135 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 6800 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| 3.5% strain | 170 | MPa | ISO 178 |
| 4.0% strain | 175 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | |||
| -40°C | 70 | kJ/m² | ISO 179 |
| 23°C | 70 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 204 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 208 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 1.60 mm | HB | UL 94, IEC 60695-11-10, -20 | |
| 3.20 mm | HB | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 700 | °C | IEC 60695-2-12 |
| 3.00 mm | 700 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 725 | °C | IEC 60695-2-13 |
| 3.00 mm | 725 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SE-165 | SHIN-A T&C | Epoxy | SHIN-A |
| Moplen EP242N | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| T-Blend® 5510N-PE | TSRC Corporation | TPE | T-Blend® |
| Alcryn® 2360 BK | Advanced Polymer Alloys | MPR | Alcryn® |
| LEXAN™ OQ1028 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |