Order Products : sales@su-jiao.com
Tislamid® PA66 PA66 UNR
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Tisan |
| Trademark: | Tislamid® PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gFH7mS_Tislamid-PA66-PA66-UNR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tislamid® PA66 PA66 UNR is a Polyamide 66 (Nylon 66) material. It is available in Africa & Middle East or Europe for injection molding. Primary attribute of Tislamid® PA66 PA66 UNR: Flame Rated. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.2 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 82 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 75.0 | MPa | |
| Break | 70.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.5 | % | |
| Break | 3.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 6.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 225 | °C | ISO 75-2/Be |
| Vicat Softening Temperature | 240 | °C | ISO 306/B120 |
| Melting Temperature | 260 to 265 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (3.00 mm) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 250 to 270 | °C | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 75.0 to 85.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PC PC1000 resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |
| Unipren® Elastomers A3 PRTA010 80A UP306 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| Petrotene® PP A3 G30 PRTA011 PH360 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |
| POLYCOMPO PE 8200B | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |
| Sylvin 8205-85UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |