TAROLON 2520
| Category: | PC , Polycarbonate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gF6LXc_TAROLON-2520.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC medium viscosity, standard grade for general purpose. UL94 V2 approved all colors at 1,6 mm Available: in natural, trasparent and opaque colors. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 to 0.70 | % | |
| Across Flow | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.12 | % | ASTM D570, ISO 62 |
| Saturation | 0.35 | % | ASTM D570 |
| Saturation, 23°C | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 62.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 85 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 85.0 | MPa | ISO 178 |
| Yield | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 25 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 3(23°C) | > 300 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 600 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 140 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/A50, ASTM D1525 4 |
| Ball Pressure Test (125°C) | Pass | VDE 0470 | |
| CLTE - Flow (-30 to 30°C) | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 20 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Ignition Temperature (2.00 mm) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 26 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 1.0 to 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | 6x4x50 mm |
| 3 . | 6x4x50 mm |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-004 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| REXtac® APAO RT 3460 | Huntsman Corporation | PAO | REXtac® APAO |
| NEFTEKHIM PP 5213M (RCXP723) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Electroblend® ABS-1800 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | ABS | Electroblend® |
| LNP™ THERMOCOMP™ PF001S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |