LNP™ LUBRICOMP™ RFL16 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | gDhBDO_LNP-LUBRICOMP-RFL16-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFL16 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% PTFE. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RFL-4016 Product reorder name: RFL16 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.43 | g/cm³ | ASTM D792 |
| -- | 1.40 | g/cm³ | ISO 1183, ASTM D792 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.57 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.88 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11000 | MPa | ASTM D638 |
| -- | 10600 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 188 | MPa | ISO 527-2/5 |
| Break 2 | 189 | MPa | ASTM D638 |
| Break | 185 | MPa | ISO 527-2/5 |
| Tensile Strain | |||
| Yield | 2.8 | % | ISO 527-2/5 |
| Break 3 | 2.8 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 8920 | MPa | ASTM D790 |
| -- 5 | 8980 | MPa | ISO 178 |
| Flexural Strength 6(Break, 50.0 mm Span) | 263 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.55 | ||
| vs. Itself - Static | 0.53 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.400 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 16.5 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 7 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 8 | 62 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 9.40 | J | ASTM D3763 |
| -- | 2.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 259 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 262 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 249 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 251 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenopom® POM B3 HF UV PRTA011 PR312 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| Alathon® L5008HP | LyondellBasell Industries | HDPE, HMW | Alathon® |
| apinat® DP2165 | API SpA | Biodeg Polymers | apinat® |
| Osterlene® PPC10-SHI | Osterman & Company | PP Impact Copolymer | Osterlene® |
| Sylvin 4240-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |